AS-KETEX filtration fabrics are manufactured from special high-twist yarn, and they have been used successfully world wide for more than 15 years. They meet highest technical requirements as guaranteed high thermal resistance of 720 °C for 4 hours. AS-KETEX also manufactured Thermo Formed Combo Bags, custom designed and woven specially for aluminium diffusion and filtration.
Widely used for Filtration of molten Aluminium in foundry of automobile wheel, motorcycle wheel, cylinder piston as well as aluminium alloy parts. AS-KETEX Thermally Formed Combo Bags does....(a) stays firm continuously for a longer time @ 1200 °C (b) have very low smoke and flame when in contact with Molten Aluminium. (c) results a are very cost effective and yields higher ROI. (d) resourcefully decrease the scuffle after the casting and smelting. (e) comprises of the high thermal resistant. (f) have effective properties to eliminate the inclusions, which results perfection of mechanical strength and surface finish.
Advantages of Thermally Formed Combo Bags. (1) Negligible Odor & Smoke during 1st contact to Molten Aluminium. (2) Diminish Scrap. (3) Eradicates Oxides. (4) Unvarying Metal Dispersal. (5) Reduces Turbulence.
|PRODUCT DESCRIPTION||WEAVE/TEXTURE||THICKNESS(mm)||GSM||THERMAL STABILITY||BREAKING LOAD (N/5 cm) MACHINE DIRECTION||BREAKING LOAD (N/5 cm) CROSS DIRECTION|
|400 Mesh Fiber Glass Filtration Fabric||Mesh||0.55 ± 0.05||350 ± 15||720||≥ 2500||≥2500|
|200 Mesh Fiber Glass Filtration Fabric||Mesh||0.58 ± 0.05||260 ± 15||720||≥ 2000||≥ 2000|